302/304 Stainless Steel balls
| Feature: |
302ss is Austenitic Stainless steel, offers excellent corrosion resistance in organic, acid, oxidizing, food environment, etc. The light magnetic properties combined with exceptionally high thoughness at all temperatures make these steels an excellent selection for many application. . Corrosion resistance is higher after annealing and passivation. No recomanded for sulphuric or halogen acid. 304 Stainless Steel has a lower carbon content than 302 Stainless Steel. 304 is slightly magnetic |
| Hardness: |
Non-annealed hardness, uniform throughout, as measured on parallel flats, is typically Rockwell "C" 25 to 39. Annealed hardness, available on request, is typically Rockwell "B" 75 to 90. |
| Size Available: |
2.0mm - 19.05mm (3/4") |
| Grade Available: |
G100 - G1000 |
| Application: |
Most of Checmical application: valves, aerosol, finger pumps, etc. |
| Material Conversion: |
ASTM/AISI |
DIN |
W-Nr. |
NF |
JIS |
|
|
302 |
X12CrNi18-18 |
1.4300 |
Z10CN18.09 |
SUS302 |
|
|
304 |
X5CrNi18-10 |
1.4301 |
Z6CN18.09 |
SUS304 |
|
|
| Chemical Composition: |
Carbon
C |
Chromium
Cr |
Manganese
Mn |
Silicon
Si |
Sulfur
S |
Phosphorus
P |
Nickel
Ni |
0.15% max. |
17.0-19.0% |
2% max. |
1% max. |
0.03% max. |
0.045% max. |
8.0-10.0% |
Mechanical Properties: |
Tensile Strength |
Yield Strength |
Modulus of Elasticity |
Density |
|
|
|
100,000-180,000 psi |
50,000 -150,000 psi |
29,000,000 psi |
0.286 lb./cu. in. |
|
|
|
|
|